                                                            環保型聚氯乙烯/丁腈復合物彈性體護套料 W-7081 W-9081 W-0581
                                                            Lead-free Elastomeric PVC / NBR Jacketing Compound...
                                                            型號:0

                                                            參考價:¥

                                                            說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
                                                            Product Description產品描述
                                                            Lead-free elastomeric PVC/NBR jacketing compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin and nitrile-butadiene rubber as the basic raw material, and add special plasticizer, stabilizer, flame retardant and other accessory ingredients.
                                                            環保型聚氯乙烯/丁腈復合物彈性體護套料是以優質聚氯乙烯樹脂和丁腈橡膠為基料,加入特種增塑劑、穩定劑、阻燃劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
                                                             
                                                            Characteristics and Application 特點及用途
                                                            These products have good oil-resistant property, soft and flexible, and good processability. They can meet RoHS Standard. They are mainly used for the jacketing of oil-resistant and flame-retardant cables, elevator cables, oil-resistant soft wires of dust cleaner, heavy soft cables and crane cables.
                                                            產品具有良好的耐油性、彈性和柔軟性,加工性能優異,符合RoHS環保標準。主要用于有耐油要求的電線電纜、電梯電纜、耐油吸塵器軟線、重型軟線、起重機電纜等護層材料。
                                                             
                                                            Processing Indicator加工工藝
                                                            Recommend to use single-screw extruders with L/D= 20-25.
                                                            建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
                                                            Model
                                                            牌號
                                                            Machine Barrel Temperature
                                                            機筒溫度
                                                            Molding Temperature
                                                            機頭溫度
                                                            W-7081 / W-9081 / W-0581 145-170℃ 165-175℃
                                                             

                                                            Physical and Electrical Properties
                                                            機械物理性能及電性能指標

                                                            Item

                                                            試驗項目

                                                            Unit
                                                            單位
                                                            Technical Requirements
                                                            技術要求
                                                            W-7081 W-9081 W-0581
                                                            Density
                                                            比重
                                                            \ ≤1.35 ≤1.35 ≤1.35
                                                            Tensile Strength
                                                            拉伸強度
                                                            MPa ≥12.5 ≥12.5 ≥12.5
                                                            Elongation at Break
                                                            斷裂伸長率
                                                            % ≥250 ≥250 ≥250
                                                            Thermal Aging
                                                            熱老化試驗
                                                            \ 80℃×168h 100℃×240h 135℃×168h
                                                            Tensile Strength Variation
                                                            拉伸強度變化率
                                                            % ±40 ±40 ±40
                                                            Elongation Variation
                                                            斷裂伸長率變化率
                                                            % ±40 ±40 ±40
                                                            Dielectric Strength
                                                            介電強度
                                                            MV/m ≥18 ≥18 ≥18
                                                            200℃Thermal Stability
                                                            200℃時熱穩定時間
                                                            min ≥80 ≥120 ≥120
                                                            20℃Volume Resistivity
                                                            20℃時體積電阻率
                                                            Ω.m ≥1×108 ≥1×108 ≥1×108
                                                            Brittle Temperature with Impact
                                                            沖擊脆化溫度
                                                            -35 -35 -35
                                                            Oil Resistance
                                                            耐油性能(ASTM 902)
                                                            Temperature of Test試驗溫度 70 100 100
                                                            Time of Test
                                                            試驗時間
                                                            h 24 24 24
                                                            Tensile Strength Variation
                                                            拉伸強度變化率
                                                            % ±40 ±40 ±40
                                                            Elongation Variation
                                                            斷裂伸長率變化率
                                                            % ±40 ±40 ±40
                                                            Hardness
                                                            硬度
                                                            Shore A ≤70 ≤70 ≤70