                                                            您所在的位置:網站首頁 > > 產品中心 > 通用PVC材料 > PVC特種料環保型聚氯乙烯耐遷移料 W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
                                                            環保型聚氯乙烯耐遷移料 W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
                                                            Lead-free Migration Resistant PVC Compound...
                                                            型號:0

                                                            參考價:¥

                                                            說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
                                                            Product Description產品描述
                                                            Lead-free migration resistant PVC compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw material, and add special plasticizer, stabilizer and other accessory ingredients.
                                                            環保型聚氯乙烯耐遷移料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、特種穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
                                                             
                                                            Characteristics and Application 特點及用途
                                                            The products have excellent migration-resistant properties and good processability. They can meet RoHS Standard. They are mainly used for the jacketing of wire and cables which have anti-PS or anti-ABS property requirements.
                                                            產品具有良好的非遷移性,加工性能優異,符合RoHS環保標準。主要用于耐PS或ABS電線電纜絕緣和護套。
                                                             
                                                            Processing Indicator加工工藝
                                                            Recommend to use single-screw extruders with L/D= 20-25.
                                                            建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
                                                            Model
                                                            牌號
                                                            Machine Barrel Temperature
                                                            機筒溫度
                                                            Molding Temperature
                                                            機頭溫度
                                                            W-7091 / W-9091 / W-0591 150-175℃ 170-185℃
                                                            W-7092 / W-9092 / W-0592 150-175℃ 170-180℃
                                                             
                                                             
                                                            Physical and Electrical Properties
                                                            機械物理性能及電性能指標

                                                            Item

                                                            試驗項目

                                                            Unit
                                                            單位
                                                            Technical Requirements
                                                            技術要求
                                                            W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
                                                            Tensile Strength
                                                            拉伸強度
                                                            MPa ≥15.0 ≥15.0 ≥15.0 ≥15.0 ≥16.0 ≥16.0
                                                            Elongation at Break
                                                            斷裂伸長率
                                                            % ≥150 ≥180 ≥150 ≥180 ≥150 ≥180
                                                            Thermal Deformation
                                                            熱變形
                                                            % ≤40 ≤50 ≤40 ≤50 ≤40 ≤50
                                                            Brittle Temperature with Impact
                                                            沖擊脆化溫度
                                                            -15 -20 -15 -20 -15 -20
                                                            200℃Thermal Stability
                                                            200℃時熱穩定時間
                                                            min ≥60 ≥60 ≥80 ≥80 ≥80 ≥80
                                                            20℃Volume Resistivity
                                                            20℃時體積電阻率
                                                            Ω.m ≥1.0×1011 ≥1.0×108 ≥1.0×1011 ≥1.0×109 ≥1.0×1011 ≥1.0×109
                                                            Dielectric Strength
                                                            介電強度
                                                            MV/m ≥20 ≥18 ≥20 ≥18 ≥20 ≥18
                                                            Thermal Aging
                                                            熱老化試驗
                                                            \ 100℃×168h 100℃×168h 100℃×240h 100℃×240h 135℃×168h 135℃×168h
                                                            Tensile strength after aging
                                                            老化后拉伸強度
                                                            MPa ≥15.0 ≥15.0 ≥15.0 ≥15.0 ≥16.0 ≥16.0
                                                            Tensile Strength Variation
                                                            拉伸強度變化率
                                                            % ±20 ±20 ±20 ±20 ±20 ±20
                                                            Elongation After Aging
                                                            老化后斷裂伸長率
                                                            % ≥150 ≥180 ≥150 ≥180 ≥150 ≥180
                                                            Elongation Variation
                                                            斷裂伸長率變化率
                                                            % ±20 ±20 ±20 ±20 ±20 ±20
                                                            Migration ResistantTest
                                                            耐遷移試驗
                                                            (55℃×168h)
                                                            \ 無污染 無污染 無污染 無污染 無污染 無污染